INEOS products make a significant contribution to saving life, improving health and enhancing standards of living for people around the world. Our businesses produce the raw materials that are essential in the manufacture of a wide variety of goods, ranging from automotive parts to medical applications, mobile phones to construction.
Showing 27 Results
INEOS Styrolution
-
MaterialSBCBrandK-Resin®BusinessINEOS StyrolutionGrades
GRADE TENSILE
MODULUS
(MPa)VICAT
SOFTENING
VST/B/50 (50°C/h, 50N)
(°C)MELT
VOLUME
RATE
220°C/10kg
(cm³/10 min)CHARPY
NOTCHED
IMPACT
STRENGTH
23°C
(MPa)TENSILE
STRESS
@ YIELD
23°C
(MPa)MORE INFO TYPICAL APPLICATIONS K-Resin BK10 1500 53 (N/A) 2 25 MORE INFO > K-Resin® BK10 process very well in injection molding, providing good cycle times and design flexibility. Applications range from containers and packaging with living hinges to medical applications, toys, displays, overcaps and hangers. INEOS Styrolution has several grades of K-Resin® SBC tailored for your injection molded needs. K-Resin DK11 1500 52 (N/A) 2 25 MORE INFO > K-Resin® DK11 makes a clear, stiff, very tough, high gloss film suitable for applications such as candy twist wrap, shrink sleeves and overwrap. K-Resin® SBC grades designed for blown film extrusion is DK11. K-Resin DK11E 1500 52 (N/A) 2 25 MORE INFO > K-Resin® DK11E makes a clear, stiff, very tough, high gloss film suitable for applications such as candy twist wrap, shrink sleeves and overwrap. K-Resin® SBC grade designed for blown film extrusion is DK11E. K-Resin KR01 1600 65 (N/A) 2 33 MORE INFO > K-Resin® KR01 process very well in injection molding, providing good cycle times and design flexibility. Applications range from containers and packaging with living hinges to medical applications, toys, displays, overcaps and hangers. INEOS Styrolution has several grades of K-Resin® SBC tailored for your injection molded needs. K-Resin KR03 1500 53 (N/A) 2 25 MORE INFO > K-Resin® KR03 process very well in injection molding, providing good cycle times and design flexibility. Applications range from containers and packaging with living hinges to medical applications, toys, displays, overcaps and hangers. INEOS Styrolution has several grades of K-Resin® SBC tailored for your injection molded needs. K-Resin KR03E 1500 53 (N/A) 2 25 MORE INFO > K-Resin® KR03E process very well in injection molding, providing good cycle times and design flexibility. Applications range from containers and packaging with living hinges to medical applications, toys, displays, overcaps and hangers. INEOS Styrolution has several grades of K-Resin® SBC tailored for your injection molded needs. K-Resin KR05 1500 53 (N/A) 2 25 MORE INFO > K-Resin® KR05 alone or in blends, can be extruded into sheet and thermoformed on conventional equipment at high output rates. The favorable economics of K-Resin® SBC, along with high productivity, have made possible tough clear disposable drinking cups, lids and other packaging applications. INEOS Styrolution has several grades of K-Resin® SBC tailored for your sheet extrusion needs. K-Resin® KR05 will process on most conventional equipment, allowing the molder to run a crystal clear bottle without expensive machine modifications, special molds, different screws, or dryers. K-Resin® SBC are blow molded in a broad range of sizes and shapes, from small pill bottles and medical drainage units, to very tall display bottles. They can also be injection blow molded into extremely high impact bottles with glass-like clarity. K-Resin KR10 (N/A) (N/A) (N/A) (N/A) (N/A) MORE INFO > K-Resin® KR10 alone or in blends, can be extruded into sheet and thermoformed on conventional equipment at high output rates. The favorable economics of K-Resin® SBC, along with high productivity, have made possible tough clear disposable drinking cups, lids and other packaging applications. INEOS Styrolution has several grades of K-Resin® SBC tailored for your sheet extrusion needs. K-Resin® KR10 will process on most conventional equipment, allowing the molder to run a crystal clear bottle without expensive machine modifications, special molds, different screws, or dryers. K-Resin® SBC are blow molded in a broad range of sizes and shapes, from small pill bottles and medical drainage units, to very tall display bottles. They can also be injection blow molded into extremely high impact bottles with glass-like clarity. K-Resin KR38 900 50 (N/A) 50 15 MORE INFO > K-Resin® KR38 alone or in blends, can be extruded into sheet and thermoformed on conventional equipment at high output rates. The favorable economics of K-Resin SBC, along with high productivity, have made possible tough clear disposable drinking cups, lids and other packaging applications. INEOS Styrolution has several grades of K-Resin SBC tailored for your sheet extrusion needs. K-Resin KR40 750 40 (N/A) 4 15 MORE INFO > K-Resin® KR40 alone or in blends, can be extruded into sheet and thermoformed on conventional equipment at high output rates. The favorable economics of K-Resin SBC, along with high productivity, have made possible tough clear disposable drinking cups, lids and other packaging applications. INEOS Styrolution has several grades of K-Resin SBC tailored for your sheet extrusion needs. K-Resin KR52 (N/A) (N/A) (N/A) (N/A) (N/A) MORE INFO > K-Resin® KR52 makes a clear, stiff, very tough, high gloss film suitable for applications such as candy twist wrap, shrink sleeves and overwrap. K-Resin® KR52 is designed for use in the uniaxial oriented film process for shrink sleeves. K-Resin KR53 (N/A) (N/A) (N/A) (N/A) (N/A) MORE INFO > K-Resin® KR53 makes a clear, stiff, very tough, high gloss film suitable for applications such as candy twist wrap, shrink sleeves and overwrap. -
MaterialSBCBrandStyroflex®BusinessINEOS StyrolutionGrades
GRADE TENSILE
MODULUS
(MPa)VICAT
SOFTENING
VST/B/50 (50°C/h, 50N)
(°C)MELT
VOLUME
RATE
220°C/10kg
(cm³/10 min)CHARPY
NOTCHED
IMPACT
STRENGTH
23°C
(MPa)TENSILE
STRESS
@ YIELD
23°C
(MPa)MORE INFO TYPICAL APPLICATIONS Styroflex 2G66 120 (N/A) (N/A) (N/A) 4 MORE INFO > Styroflex® 2G66 is a styrene-butadiene block copolymer (SBC) with the properties of a thermoplastic elastomer (S-TPE) suitable for extrusion (blown and cast film) and for injection molding. Styroflex® 2G66 is also used for polymers modification and compatibilization. It is more polar than comparable SBS or SEBS grades and offers a combination of high resilience and toughness with good transparency and process stability. Styroflex 2G66 LE 120 (N/A) (N/A) (N/A) 4 MORE INFO > Styroflex® 2G66 LE is a styrene-butadiene block copolymer (SBC) with the properties of a thermoplastic elastomer (S-TPE) suitable for extrusion (blown and cast film) and for injection molding. Styroflex® 2G66 LE is a grade with reduced residuals to achieve improved VOC levels for demanding applications. It can be used for polymer modification and compatibilization. It is more polar than comparable SBS or SEBS grades and offers a combination of high resilience and toughness with good transparency and process stability. Styroflex 4G80 (N/A) (N/A) (N/A) 80 (N/A) MORE INFO > Styroflex® 4G80 is a styrene butadiene block copolymer (SBC) optimized for extrusion. -
MaterialSBCBrandStyrolux®BusinessINEOS StyrolutionGrades
GRADE TENSILE
MODULUS
(MPa)VICAT
SOFTENING
VST/B/50 (50°C/h, 50N)
(°C)MELT
VOLUME
RATE
220°C/10kg
(cm³/10 min)CHARPY
NOTCHED
IMPACT
STRENGTH
23°C
(MPa)TENSILE
STRESS
@ YIELD
23°C
(MPa)MORE INFO TYPICAL APPLICATIONS Styrolux 3G46 1550 51 (N/A) 3 27 MORE INFO > Styrolux® 3G46 is a clear styrene-butadiene copolymer (SBC) developed specifically for sheet- and film extrusion and for thermoformed articles. Styrolux® 3G46 is designed for improved performance in blends with general-purpose polystyrene, providing parts with an excellent balance of transparency and toughness. Styrolux 3G55 900 35 (N/A) 85 15 MORE INFO > Styrolux® 3G55 is a clear styrene butadiene copolymer (SBC) used mainly in sheet extrusion and thermoforming applications. It is specifically designed for improved performance in blends with general-purpose polystyrene, providing parts with an excellent balance of toughness, transparency and economics. Because of the tendency of blocking, 3G55 is mainly used in inline thermoforming. 3G55 is difficult to print and decorate since it contains a microcrystalline wax. Styrolux 4G60 900 45 (N/A) 4 14 MORE INFO > Styrolux 4G60 is a new clear styrene-butadiene copolymer (SBC) designed specifically for in-jection molding of parts with an excellent balance of transparency and ductility. Styrolux 656C 1800 63 (N/A) 2 35 MORE INFO > Styrolux® 656C is a clear styrene-butadiene copolymer (SBC) with enhanced flow properties. It is used almost exclusively for injection molding of rigid, tough parts requiring highest levels of clarity and surface gloss. Styrolux® 656C is sterilizable by gamma-rays and offers good hinge properties. Styrolux 684D 1500 59 (N/A) 4 26 MORE INFO > Styrolux® 684D is a clear styrene-butadiene copolymer (SBC) used in injection molding for parts with enhanced toughness as well as in sheet and film extrusion and blow molding.Parts made of Styrolux® 684D reveal excellent printability. Styrolux 693D (N/A) 48 (N/A) 5 22 MORE INFO > Styrolux® 693D is a clear styrene-butadiene copolymer (SBC) with a well balanced combination of toughness and clarity. Styrolux 693D is mainly used for thermoformed articles, especially in blends with general-purpose polystyrene. Styrolux® 693D contains a microcrystalline wax which acts as an antiblock providing processing benefits but decreases the printability. Styrolux BATCH ASE (N/A) (N/A) (N/A) (N/A) (N/A) MORE INFO > Highly effective lubricants in Styrolux® Batch ASE improve the release properties of injection molded parts made from Styrolux® or Styrolux® containing blends (e.g. those with GPPS).Styrolux® Batch ASE further improves the unstacking performance of deep-drawn parts and reduces the mar sensitivity of Styrolux®. The dosing of Styrolux® Batch ASE should not exceed 4 %; in most cases 2 % is already quite sufficient to form a lubricating layer. Styrolux® Batch ASE is based on Styrolux 684D carrier. Styrolux BATCH NB10 (N/A) (N/A) (N/A) (N/A) (N/A) MORE INFO > Styrolux® Batch NB 10 contains an extremely active wax system which should be added in an amount of 0.5 % to 2 % if sheet or film blocking issues are encountered with Styrolux or Styrolux/GPPS blends. If the quantity added is too high, difficulties may occur during printing. Styrolux® Batch NB 10 is based on a GPPS-carrier. Styrolux M 1700 60 (N/A) 3 30 MORE INFO > Styrolux® M is a new, clear and rigid styrene-butadiene copolymer (SBC) designed specifically for shrink film applications. Styrolux® has been developed for blending with other SBC components like Styrolux® S, which increases the stiffness of the film and Styrolux® T1, which increases the toughness of the film. Styrolux® M is used to tailor-made the ultimate shrinkage while keeping the mechanical properties. Styrolux S 2900 64 (N/A) 2 (N/A) MORE INFO > Styrolux® S is a new developmental, clear styrene-butadiene copolymer (SBC) designed specifically for blending with Styrolux® T in order to enable high performance film extrusion and shrink film applications. As Styrolux® S is blended with Styrolux® T it increases the stiffness of the film and improves the storage stability of film reels (reduced natural shrinkage). Styrolux T 1200 46 75 2 25 MORE INFO > Styrolux® T is a new developmental, clear and tough styrene-butadiene copolymer (SBC) designed specifically for high performance film extrusion and shrink film applications. Styrolux® T has been developped for blending with a second SBC component, Styrolux® S, which inceases the stiffness of the film and improves the storage stability of film reels (reduced natural shrinkage). Styrolux T1 1100 48 75 (N/A) 25 MORE INFO > Styrolux® T1 is a new, clear and tough styrene-butadiene copolymer (SBC) designed specifically for high performance film extrusion and shrink film applications. Styrolux® T1 has been developed for blending with a sceond SBC component, Styrolux® S, which increases the stiffness of the film and improves the storage stability of film reels (reduced natural shrinkage).